Mortar Modifier - Mortar Modifier Exporter, Importer, Manufacturer, Service Provider, Distributor, Supplier, Trading Company, Ahmedabad, India

Product Code : 06

Product Specification

Mortar Modifier

Styrene Butadiene Rubber Latex Polymer Dispersion. Morter Modifier

MAXBOND S.B.R is a highly modified, Milky white latex rubber polymer based product specially formulated to achieve high tensile, shear and flexural strength by using as a mortar modifier, widely used for hydraulic setting agent particularly cement mixtures for high performance water proofing.

Advantages

Excellent compatibility with cement, ground quartz, fine sand, micro dolomite
Non-yellowing and has excellent resistance to ultra violet degradation so ideal for G.R.C work.
Imparts flexibility of mortar.
High adhesion properties
High durable concrete work.
Excellent improved tensile, flexural and shear strength.
Excellent waterproofing properties.
Abrasion and wide range of chemical resistance.
Reduces shrinkage, cracks and providing non-porous surface.
High resistance against carbonation
Resistance against most of alkalis, solvents, salt and industrial chemicals.
Eliminates wet curing

Technical Specifications

Appearance: Milky white
Solid contains: 50 to 52%
Viscosity: 60-250 mPaS (Brookefield RVT DV-IISpindle 2/60rpm)
Density: 1.02 g/cm3
PH: 7.8to10
Minimum film forming temp: 160 C

Recommended For

As a mortar modifier in patching work. And high performance waterproofing.
As a bonding agent with old to new concrete work
For waterproofing of R.C.C work as well as impart strength.
To improve strength in RCC heavy duty floor and screeds and toppings.
Recommended as a additive with tile fixing and joint filling mortar to achieve high strength and waterproof durable tile work.
High rise RCC structural framework.
Dams and cannels, RCC road and high way constructions

How To Apply As A Bonding Agent

Surface must be clean, away from grease, oil dust or other contaminates, dampened with water so that although none is visible,

It is recommended the fresh concrete be applied as soon as possible after applying the latex, satisfactory bonds have been obtained when the fresh concrete was applied up to seven days after application of latex. Providing the latex film has not become dirty.

Can be applied either by brush, roller and spraying.

As A Polymer Modifier For Hydraulic Cement Mixtures

Addition of MAXBOND S.B.R to Portland cement mixtures increases the bond strength, flexural strength permeability resistance carbonation resistance and acid resistance of the hardened mixture.

Safety

Attention should be paid to the normal precautions for handling chemicals and to the measured prescribed in the local health regulations. The place of work must be ventilated, skin care measured should be adopted and safety goggles should be worn.

MAXBOND S.B.R is not a hazardous product as per our guideline for classifications, and is does not pose any risk to health when used for the purpose for which it is intended and principles of sound industrial practice are observed.

Storage
Do not keep under direct sunlight, must be stored undertightly closed containers ortanks. and should not be allowed to come into contact with any unprotected metals except stainless steel during storage and processing.

Shelf Life
1 year in factory sealed packing.

Packing
1,5,20and 50 liters

Polymer Modifier For Hydraulic Cement Mixtures

Purpose	Standard Mixing Ratio				Coating Bed	Coating
Purpose	Cement	Sand	Max. S.B.R	Watere	Thickness	Coating
Polymer dispersion mortar	40 kg	120 kg	6-8 kg	5-7 kg	Concrete ALC Board	5-10 mm
Thin-coating mortar	40 kg	120 kg	6-8 kg	5-7 kg	Concrete ALC Board	5-10 mm

Coverage

Adhesion Surface	Blending Ratio		Coating
Adhesion Surface	Max - S.B.R	Water	Coating
Wall concrete	1	2	120-150 g/m2
Floor concrete	1	3	200-250 g/m2
Wall, Floor-ALC	1	4	400-450 g/m2